Physical properties | Standard | Value | Measure Units |
---|---|---|---|
Density | ISO 1183 | 1.53 | g/cm³ |
Linear shrinkage at moulding | |||
Longitudinal (2.0mm/60MPa) | ISO 294-4 | 0.30 ÷ 0.55 | % |
Transversal (2.0mm/60MPa) | ISO 294-4 | 1.00 ÷ 1.30 | % |
Dimensional stability | --- | 45 | |
Moisture absorption | |||
Saturation, in air | ISO 62-4 | 0.16 | % |
Mechanical properties | Standard | Value | Measure Units |
CHARPY impact strength | |||
Unnotched, at +23°C | ISO 179-1eU | 50 | kJ/m² |
Unnotched, at -20°C | ISO 179-1eU | 35 | kJ/m² |
Notched, at +23°C | ISO 179-1eA | 8 | kJ/m² |
Notched, at -20°C | ISO 179-1eA | 4 | kJ/m² |
Tensile elongation | |||
At break (5 mm/min), 23°C | ISO 527 | 2.3 | % |
At break (5 mm/min), 60°C | ISO 527 | 3 | % |
At break (5 mm/min), 90°C | ISO 527 | 5.3 | % |
At break (5 mm/min), 120°C | ISO 527 | 6 | % |
At break (5 mm/min), 150°C | ISO 527 | 6 | % |
Tensile strength | |||
At break (5 mm/min), 23°C | ISO 527 | 125 | MPa |
At break (5 mm/min), 60°C | ISO 527 | 85 | MPa |
At break (5 mm/min), 90°C | ISO 527 | 60 | MPa |
At break (5 mm/min), 120°C | ISO 527 | 50 | MPa |
At break (5 mm/min), 150°C | ISO 527 | 40 | MPa |
Elastic modulus | |||
Tensile (1 mm/min), 23°C | ISO 527 | 10300 | MPa |
Tensile (1 mm/min), 60°C | ISO 527 | 8000 | MPa |
Tensile (1 mm/min), 90°C | ISO 527 | 5000 | MPa |
Tensile (1 mm/min), 120°C | ISO 527 | 3600 | MPa |
Tensile (1 mm/min), 150°C | ISO 527 | 2500 | MPa |
Thermal properties | Standard | Value | Measure Units |
Coefficient of linear thermal expansion (CLTE) | |||
+30°C to +100°C (longitudinal) | ISO 11359 | 30 | × 10ˉ⁶ Kˉ¹ |
+30°C a +100°C (transversal) | ISO 11359 | 70 | × 10ˉ⁶ Kˉ¹ |
VICAT - Softening point | |||
50N (heating rate 120°C/h) | ISO 306 | 215 | °C |
HDT - Heat Deflection Temperature | |||
0.45 MPa | ISO 75 | 220 | °C |
1.81 MPa | ISO 75 | 210 | °C |
Thermal conductivity | |||
in plane | ASTM E 1461-92 | 0.2 | W/mK |
through plane | ASTM E 1461-92 | 0.2 | W/mK |
Flammability | Standard | Value | Measure Units |
Oxygen Index | ASTM D 2863 | 23 | % |
Flammability rating | |||
3 mm thickness | UL 94 | HB | |
1.5 mm thickness | UL 94 | HB | |
0.75 mm thickness | UL 94 | HB | |
Electrical properties | Standard | Value | Measure Units |
CTI - Comparative Tracking Index - solution A (without surfactant) | IEC 60112 | 475 | V |
Electrical resistivity | |||
Surface, dry | ASTM D 257 / D 4496 | 1E12 | ohm |
Dielectric strength (short period) | |||
2 mm thickness, 23°C, dry | ASTM D 149 | 30 | kV/mm |
Melt Temperature | Standard | Value | Measure Units |
Suggested melt temperature | --- | 240 ÷ 250 | °C |
Mould Temperature | Standard | Value | Measure Units |
Suggested mould temperature | --- | 60 ÷ 100 | °C |