Physical properties | Standard | Value | Measure Units |
---|---|---|---|
Density | ISO 1183 | 1.19 | g/cm³ |
Linear shrinkage at moulding | |||
Longitudinal (2.0mm/60MPa) | ISO 294-4 | 0.90 ÷ 1.10 | % |
Transversal (2.0mm/60MPa) | ISO 294-4 | 0.90 ÷ 1.10 | % |
Dimensional stability | --- | 80 | |
Moisture absorption | |||
Saturation, in air | ISO 62-4 | 2.35 | % |
Mechanical properties | Standard | Value | Measure Units |
CHARPY impact strength | |||
Unnotched, at +73°F | ISO 179-1eU | 25 | ft.lb/in² |
Notched, at +73°F | ISO 179-1eA | 3.5 | ft.lb/in² |
Tensile elongation | |||
At break (5 mm/min), 73°F | ISO 527 | 2.8 | % |
Tensile strength | |||
At break (5 mm/min), 73°F | ISO 527 | 10500 | psi |
Elastic modulus | |||
Tensile (1 mm/min), 73°F | ISO 527 | 510 | kpsi |
Thermal properties | Standard | Value | Measure Units |
Coefficient of linear thermal expansion (CLTE) | |||
+30°C to +100°C (longitudinal) | ISO 11359 | 65 | × 10⁶ K¹ |
+30°C a +100°C (transversal) | ISO 11359 | 75 | × 10⁶ K¹ |
VICAT - Softening point | |||
50N (heating rate 120°C/h) | ISO 306 | 365 | °F |
HDT - Heat Deflection Temperature | |||
0.45 MPa | ISO 75 | 383 | °F |
1.81 MPa | ISO 75 | 266 | °F |
Electrical properties | Standard | Value | Measure Units |
Electrical resistivity | |||
Surface, dry | ASTM D 257 | 6E8 | ohm |
Melt Temperature | Standard | Value | Measure Units |
Suggested melt temperature | --- | 480 ÷ 520 | °F |
Mould Temperature | Standard | Value | Measure Units |
Suggested mould temperature | --- | 175 ÷ 210 | °F |