LARTON AM K/10

Family: LATI AM
Base resin:Polyphenylene Sulphide (PPS)
General information
Compound based on Polyphenylene Sulphide (PPS). 3D printing version. Carbon fibres. Intrinsically flame retardant. PFAS-free product.
The products mentioned herein are not suitable for applications in contact with foodstuffs or for potable water transportation, or for toy manufacturing.
The products mentioned herein are not suitable for applications in the pharmaceutical, medical or dental sector.
Features
  • - Intrinsically flame retardant.
Project challenges
  • - High temperature usage
  • - Flame retardancy halogen free
  • - Chemical stability
  • - Wear and friction
Additives
  • - Carbon fibres
Process types
  • - 3D Printing
Download documents
Technical datasheets
  • IT
  • UK
  • US
  • DE
  • FR
  • ES
  • PT
Technical characteristics
Physical properties Standard Value Measure Units
Density ISO 1183 1.34 g/cm³
Linear shrinkage at moulding
Longitudinal (2.0mm/60MPa) ISO 294-4 0,10 ÷ 0,20 %
Transversal (2.0mm/60MPa) ISO 294-4 0,55 ÷ 0,85 %
Dimensional stability --- 40
Moisture absorption
Saturation, in air ISO 62-4 0.03 %
Mechanical properties Standard Value Measure Units
CHARPY impact strength
Unnotched, at +23°C ISO 179-1eU 30 kJ/m²
Notched, at +23°C ISO 179-1eA 4 kJ/m²
Tensile elongation
At break (5 mm/min), 23°C ISO 527 1.8 %
Tensile strength
At break (5 mm/min), 23°C ISO 527 150 MPa
Elastic modulus
Tensile (1 mm/min), 23°C ISO 527 11500 MPa
Thermal properties Standard Value Measure Units
Coefficient of linear thermal expansion (CLTE)
+30°C to +100°C (longitudinal) ISO 11359 7 × 10⁶ K¹
+30°C a +100°C (transversal) ISO 11359 30 × 10⁶ K¹
VICAT - Softening point
50N (heating rate 120°C/h) ISO 306 255 °C
HDT - Heat Deflection Temperature
0.45 MPa ISO 75 275 °C
1.81 MPa ISO 75 260 °C
Thermal conductivity
in plane ASTM E 1461-92 0.5 W/mK
through plane ASTM E 1461-92 0.3 W/mK
Flammability Standard Value Measure Units
Oxygen Index ASTM D 2863 45 %
Flammability rating
3 mm thickness UL 94 V-0
1.5 mm thickness UL 94 V-0
0.75 mm thickness UL 94 V-0
GWFI - Glow Wire Flammability Index
2 mm thickness IEC 60695-2-12 960 °C
1 mm thickness IEC 60695-2-12 960 °C
GWIT - Glow Wire Ignition Test
2 mm thickness IEC 60695-2-13 775 °C
1 mm thickness IEC 60695-2-13 775 °C
Electrical properties Standard Value Measure Units
CTI - Comparative Tracking Index - solution A (without surfactant) IEC 60112 125 V
Electrical resistivity
Surface, dry ASTM D 257 1E3 ohm
Dielectric strength (short period)
2 mm thickness, 23°C, dry ASTM D 149 5 kV/mm
Melt Temperature Standard Value Measure Units
Suggested melt temperature --- NULL °C
Mould Temperature Standard Value Measure Units
Suggested mould temperature --- NULL °C
Drying conditions (hot air dessiccator)
Predrying needed. At least 4 hours at 100°C
Injection speed
Injection speed: NULL. Setting an injection profile should improve moulding.
Hot runners
Usage of hot runner: not suggested