Family: LATI MDT
Base resin:Thermoplastic elastomer (TPE)
General information
Compound based on Thermoplastic Polyurethane (TPU). Magnetic detectable filler. PFAS-free product.
The products mentioned herein are suitable for applications in contact with foodstuffs or for toy manufacturing. Nevertheless, manufactured parts have to be verified according to the specific directives.
The products mentioned herein are not suitable for applications in the pharmaceutical, medical or dental sector.
Features
- - Magnetically detectable
Additives
- - Ceramic fillers
- - Metallic powder
Download documents
Technical datasheets
- IT
- UK
- US
- DE
- FR
- ES
- PT
Technical characteristics
| Physical properties | Standard | Value | Measure Units |
|---|---|---|---|
| Density | ISO 1183 | 1.51 | g/cm³ |
| Linear shrinkage at moulding | |||
| Longitudinal (2.0mm/60MPa) | ISO 294-4 | 0.80 ÷ 1.10 | % |
| Transversal (2.0mm/60MPa) | ISO 294-4 | 0.80 ÷ 1.10 | % |
| Dimensional stability | --- | 75 | |
| Moisture absorption | |||
| Saturation, in air | ISO 62-4 | 0.25 | % |
| Mechanical properties | Standard | Value | Measure Units |
| Tensile strength | |||
| At yield (5 mm/min), 23°C | ISO 527 | 4 | MPa |
| Elastic modulus | |||
| Tensile (1 mm/min), 23°C | ISO 527 | 20 | MPa |
| Electrical properties | Standard | Value | Measure Units |
| Electrical resistivity | |||
| Surface, dry | ASTM D 257 / D 4496 | 1E12 | ohm |
| Dielectric strength (short period) | |||
| 2 mm thickness, 23°C, dry | ASTM D 149 | 19 | kV/mm |
| Melt Temperature | Standard | Value | Measure Units |
| Suggested melt temperature | --- | 205 ÷ 220 | °C |
| Mould Temperature | Standard | Value | Measure Units |
| Suggested mould temperature | --- | 20 ÷ 70 | °C |
Drying conditions (hot air dessiccator)
Predrying needed. At least 3 hours at 80 ÷ 90°C
Injection speed
Injection speed: low to medium. Setting an injection profile should improve moulding.
Hot runners
Usage of hot runner: possible
LASTANE 30 MDT07-01 BLUE:7563F1