Family: LATI MDT
Base resin:Thermoplastic elastomer (TPE)
General information
Compound based on Thermoplastic Polyurethane (TPU). Magnetic detectable filler. PFAS-free product.
Versions of product mentioned herein are suitable for applications in contact with foodstuffs or for potable water transportation, or for toy manufacturing. Nevertheless, manufactured parts have to be verified according to the specific directives.
The products mentioned herein are not suitable for applications in the pharmaceutical, medical or dental sector.
Features
- - Magnetically detectable
Project challenges
- - Metal detection
Additives
- - Ceramic fillers
- - Metallic powder
Process types
- - Injection moulding
Download documents
Technical datasheets
- IT
- UK
- US
- DE
- FR
- ES
- PT
Technical characteristics
| Physical properties | Standard | Value | Measure Units |
|---|---|---|---|
| Density | ISO 1183 | 1.5 | g/cm³ |
| Moisture absorption | |||
| Saturation, in air | ISO 62-4 | 0.3 | % |
| Mechanical properties | Standard | Value | Measure Units |
| CHARPY impact strength | |||
| Unnotched, at +23°C | ISO 179-1eU | NB | kJ/m² |
| Notched, at +23°C | ISO 179-1eA | NB | kJ/m² |
| Tensile elongation | |||
| At yield (5 mm/min), 23°C | ISO 527 | >10 | % |
| At break (5 mm/min), 23°C | ISO 527 | >50 | % |
| Tensile strength | |||
| At yield (5 mm/min), 23°C | ISO 527 | 7 | MPa |
| At break (5 mm/min), 23°C | ISO 527 | NB | MPa |
| Elastic modulus | |||
| Tensile (1 mm/min), 23°C | ISO 527 | 40 | MPa |
| Electrical properties | Standard | Value | Measure Units |
| Electrical resistivity | |||
| Surface, dry | ASTM D 257 | 1E12 | ohm |
| Dielectric strength (short period) | |||
| 2 mm thickness, 23°C, dry | ASTM D 149 | 19 | kV/mm |
| Electromagnetic reflection (Bekiscan - CP) | --- | 95 | % |
| Melt Temperature | Standard | Value | Measure Units |
| Suggested melt temperature | --- | 200 ÷ 230 | °C |
| Mould Temperature | Standard | Value | Measure Units |
| Suggested mould temperature | --- | 20 ÷ 50 | °C |
Drying conditions (hot air dessiccator)
Predrying needed. At least 3 hours at 80 ÷ 90°C
Injection speed
Injection speed: low to medium. Setting an injection profile should improve moulding.
Hot runners
Usage of hot runner: possible
LASTANE 50 MDT05-01 BLUE:7532F1