LASTILAC 11 G/10

Family: LASTILAC 11
Base resin:ABS/PC Blend (ABS/PC)
General information
Compound based on ABS/PC Blend (ABS/PC). Glass fibres. PFAS-free product.
The products mentioned herein are not suitable for applications in contact with foodstuffs or for potable water transportation, or for toy manufacturing.
The products mentioned herein are not suitable for applications in the pharmaceutical, medical or dental sector.
Features
  • - Toughened
Project challenges
  • - Improved resilience at low temperature
Additives
  • - Glass fibres
Process types
  • - Injection moulding
Download documents
Technical datasheets
  • IT
  • UK
  • US
  • DE
  • FR
  • ES
  • PT
Technical characteristics
Physical properties Standard Value Measure Units
Density ISO 1183 1.19 g/cm³
Linear shrinkage at moulding
Longitudinal (2.0mm/60MPa) ISO 294-4 0.35 ÷ 0.55 %
Transversal (2.0mm/60MPa) ISO 294-4 0.55 ÷ 0.75 %
Dimensional stability --- 58
Moisture absorption
Saturation, in air ISO 62-4 0.15 %
Mechanical properties Standard Value Measure Units
CHARPY impact strength
Unnotched, at +23°C ISO 179-1eU 30 kJ/m²
Notched, at +23°C ISO 179-1eA 12 kJ/m²
Tensile elongation
At yield (5 mm/min), 23°C ISO 527 2.3 %
At yield (5 mm/min), 60°C ISO 527 2.1 %
At yield (5 mm/min), 90°C ISO 527 1.8 %
At yield (5 mm/min), 120°C ISO 527 1.6 %
At break (5 mm/min), 23°C ISO 527 2.6 %
At break (5 mm/min), 60°C ISO 527 2.3 %
At break (5 mm/min), 90°C ISO 527 2.1 %
At break (5 mm/min), 120°C ISO 527 1.9 %
Tensile strength
At yield (5 mm/min), 23°C ISO 527 90 MPa
At yield (5 mm/min), 60°C ISO 527 50 MPa
At yield (5 mm/min), 90°C ISO 527 40 MPa
At yield (5 mm/min), 120°C ISO 527 15 MPa
At break (5 mm/min), 23°C ISO 527 70 MPa
At break (5 mm/min), 60°C ISO 527 35 MPa
At break (5 mm/min), 90°C ISO 527 25 MPa
At break (5 mm/min), 120°C ISO 527 5 MPa
Elastic modulus
Tensile (1 mm/min), 23°C ISO 527 3900 MPa
Tensile (1 mm/min), 60°C ISO 527 3600 MPa
Tensile (1 mm/min), 90°C ISO 527 3300 MPa
Tensile (1 mm/min), 120°C ISO 527 1300 MPa
Thermal properties Standard Value Measure Units
Coefficient of linear thermal expansion (CLTE)
+30°C to +100°C (longitudinal) ISO 11359 30 × 10ˉ⁶ Kˉ¹
+30°C a +100°C (transversal) ISO 11359 60 × 10ˉ⁶ Kˉ¹
VICAT - Softening point
50N (heating rate 120°C/h) ISO 306 125 °C
HDT - Heat Deflection Temperature
0.45 MPa ISO 75 130 °C
1.81 MPa ISO 75 115 °C
Flammability Standard Value Measure Units
Flammability rating
3 mm thickness UL 94 HB
1.5 mm thickness UL 94 HB
Electrical properties Standard Value Measure Units
CTI - Comparative Tracking Index - solution A (without surfactant) IEC 60112 350 V
Electrical resistivity
Surface, dry ASTM D 257 / D 4496 1E12 ohm
Dielectric strength (short period)
2 mm thickness, 23°C, dry ASTM D 149 24 kV/mm
Melt Temperature Standard Value Measure Units
Suggested melt temperature --- 250 ÷ 290 °C
Mould Temperature Standard Value Measure Units
Suggested mould temperature --- 50 ÷ 80 °C
Drying conditions (hot air dessiccator)
Predrying needed. At least 3 hours at 80 ÷ 100°C
Injection speed
Injection speed: medium. Setting an injection profile should improve moulding.
Hot runners
Usage of hot runner: possible