LATAMID 6 H-V0

Family: LATAMID 6
Base resin:Polyamide 6 (PA 6)
General information
Compound based on Polyamide 6 (PA 6). Flame retardant, UL94 V-0 class, free of halogens-based flame retardants and red phosphorous. PFAS-free product.
The products mentioned herein are not suitable for applications in contact with foodstuffs or for potable water transportation, or for toy manufacturing.
The products mentioned herein are not suitable for applications in the pharmaceutical, medical or dental sector.
Features
  • - Flame retardant, free of halogens-based flame retardants and red phosphorous
Process types
  • - Injection moulding
Download documents
Technical datasheets
  • IT
  • UK
  • US
  • DE
  • FR
  • ES
  • PT
Technical characteristics
Physical properties Standard Value Measure Units
Density ISO 1183 1.16 g/cm³
Linear shrinkage at moulding
Longitudinal (2.0mm/60MPa) ISO 294-4 1,00 ÷ 1,30 %
Transversal (2.0mm/60MPa) ISO 294-4 1,10 ÷ 1,35 %
Dimensional stability --- 75
Moisture absorption
Saturation, in air ISO 62-4 2.3 %
Mechanical properties Standard Value Measure Units
CHARPY impact strength
Notched, at +23°C ISO 179-1eA 3 kJ/m²
Tensile elongation
At yield (5 mm/min), 23°C ISO 527 3.5 %
At yield (5 mm/min), 60°C ISO 527 3.7 %
At yield (5 mm/min), 90°C ISO 527 5 %
At yield (5 mm/min), 120°C ISO 527 5 %
At break (5 mm/min), 23°C ISO 527 28 %
Tensile strength
At yield (5 mm/min), 23°C ISO 527 70 MPa
At yield (5 mm/min), 60°C ISO 527 25 MPa
At yield (5 mm/min), 90°C ISO 527 20 MPa
At yield (5 mm/min), 120°C ISO 527 15 MPa
At break (5 mm/min), 23°C ISO 527 55 MPa
Elastic modulus
Tensile (1 mm/min), 23°C ISO 527 3500 MPa
Tensile (1 mm/min), 60°C ISO 527 1500 MPa
Tensile (1 mm/min), 90°C ISO 527 650 MPa
Tensile (1 mm/min), 120°C ISO 527 500 MPa
Thermal properties Standard Value Measure Units
Coefficient of linear thermal expansion (CLTE)
+30°C to +100°C (longitudinal) ISO 11359 85 × 10⁶ K¹
+30°C a +100°C (transversal) ISO 11359 85 × 10⁶ K¹
VICAT - Softening point
50N (heating rate 120°C/h) ISO 306 200 °C
HDT - Heat Deflection Temperature
0.45 MPa ISO 75 185 °C
1.81 MPa ISO 75 60 °C
Thermal conductivity
in plane ASTM E 1461-92 0.3 W/mK
through plane ASTM E 1461-92 0.3 W/mK
Flammability Standard Value Measure Units
Oxygen Index ASTM D 2863 36 %
Flammability rating
3 mm thickness UL 94 V-0
1.5 mm thickness UL 94 V-0
0.75 mm thickness UL 94 V-0
GWFI - Glow Wire Flammability Index
2 mm thickness IEC 60695-2-12 960 °C
1 mm thickness IEC 60695-2-12 960 °C
Electrical properties Standard Value Measure Units
Electrical resistivity
Surface, dry ASTM D 257 1E12 ohm
Dielectric strength (short period)
2 mm thickness, 23°C, dry ASTM D 149 19 kV/mm
Melt Temperature Standard Value Measure Units
Suggested melt temperature --- 230 ÷ 250 °C
Mould Temperature Standard Value Measure Units
Suggested mould temperature --- 60 ÷ 90 °C
Storage
PAY ATTENTION! Material is prone to absorb moisture.
Drying conditions (hot air dessiccator)
Predrying needed. At least 2 hours at 70 ÷ 90°C
Injection speed
Injection speed: medium to high. Setting an injection profile should improve moulding.
Hot runners
Usage of hot runner: possible