LATAMID 66 VH2 G/15

Family: LATAMID 66
Base resin:Polyamide 66 (PA 66)
General information
Compound based on Polyamide 66 (PA 66). Glass fibres. PFAS-free product.
The products mentioned herein are not suitable for applications in contact with foodstuffs or for potable water transportation, or for toy manufacturing.
The products mentioned herein are not suitable for applications in the pharmaceutical, medical or dental sector.
Additives
  • - Glass fibres
Process types
  • - Injection moulding
Download documents
Technical datasheets
  • IT
  • UK
  • US
  • DE
  • FR
  • ES
  • PT
Technical characteristics
Physical properties Standard Value Measure Units
Density ISO 1183 1.24 g/cm³
Linear shrinkage at moulding
Longitudinal (2.0mm/60MPa) ISO 294-4 0.85 ÷ 1.15 %
Transversal (2.0mm/60MPa) ISO 294-4 1.00 ÷ 1.30 %
Dimensional stability --- 65
Moisture absorption
Saturation, in air ISO 62-4 2.1 %
Mechanical properties Standard Value Measure Units
CHARPY impact strength
Unnotched, at +23°C ISO 179-1eU 15 kJ/m²
Notched, at +23°C ISO 179-1eA 2 kJ/m²
Tensile elongation
At break (5 mm/min), 23°C ISO 527 2 %
Tensile strength
At break (5 mm/min), 23°C ISO 527 70 MPa
Elastic modulus
Tensile (1 mm/min), 23°C ISO 527 4300 MPa
Thermal properties Standard Value Measure Units
Coefficient of linear thermal expansion (CLTE)
+30°C to +100°C (longitudinal) ISO 11359 60 × 10ˉ⁶ Kˉ¹
+30°C a +100°C (transversal) ISO 11359 75 × 10ˉ⁶ Kˉ¹
VICAT - Softening point
50N (heating rate 120°C/h) ISO 306 245 °C
HDT - Heat Deflection Temperature
0.45 MPa ISO 75 235 °C
1.81 MPa ISO 75 100 °C
Flammability Standard Value Measure Units
Flammability rating
3 mm thickness UL 94 HB
0.75 mm thickness UL 94 HB
Electrical properties Standard Value Measure Units
Electrical resistivity
Surface, dry ASTM D 257 / D 4496 1E12 ohm
Dielectric strength (short period)
2 mm thickness, 23°C, dry ASTM D 149 19 kV/mm
Melt Temperature Standard Value Measure Units
Suggested melt temperature --- 280 ÷ 300 °C
Mould Temperature Standard Value Measure Units
Suggested mould temperature --- 80 ÷ 100 °C
Storage
PAY ATTENTION! Material is prone to absorb moisture.
Drying conditions (hot air dessiccator)
Predrying needed. At least 2 hours at 80 ÷ 100°C
Injection speed
Injection speed: medium to high. Setting an injection profile should improve moulding.
Hot runners
Usage of hot runner: possible