LATAN 13

Family: LATAN
Base resin:Polyoximethylene (POM)
General information
Product made of Polyoximethylene (POM). Unfilled. PFAS-free product.
The products mentioned herein are not suitable for applications in contact with foodstuffs or for potable water transportation, or for toy manufacturing.
The products mentioned herein are not suitable for applications in the pharmaceutical, medical or dental sector.
Features
  • - Self lubricant
Additives
  • - Unfilled
Process types
  • - Injection moulding
Download documents
Technical datasheets
  • IT
  • UK
  • US
  • DE
  • FR
  • ES
  • PT
Technical characteristics
Physical properties Standard Value Measure Units
Density ISO 1183 1.41 g/cm³
Linear shrinkage at moulding
Longitudinal (2.0mm/60MPa) ISO 294-4 2,00 ÷ 2,30 %
Transversal (2.0mm/60MPa) ISO 294-4 2,05 ÷ 2,25 %
Dimensional stability --- 70
Moisture absorption
Saturation, in air ISO 62-4 0.22 %
Melt Flow Index (MFI) ASTM D 1238 13,00@190°C/2,16kg g/10'
Mechanical properties Standard Value Measure Units
CHARPY impact strength
Notched, at +23°C ISO 179-1eA 7 kJ/m²
Notched, at -20°C ISO 179-1eA 5 kJ/m²
Tensile elongation
At break (5 mm/min), 23°C ISO 527 40 %
Tensile strength
At yield (5 mm/min), 23°C ISO 527 55 MPa
At yield (5 mm/min), 60°C ISO 527 40 MPa
At yield (5 mm/min), 90°C ISO 527 30 MPa
At break (5 mm/min), 23°C ISO 527 50 MPa
Elastic modulus
Tensile (1 mm/min), 23°C ISO 527 2000 MPa
Tensile (1 mm/min), 60°C ISO 527 1500 MPa
Tensile (1 mm/min), 90°C ISO 527 850 MPa
Thermal properties Standard Value Measure Units
Coefficient of linear thermal expansion (CLTE)
+30°C to +100°C (longitudinal) ISO 11359 110 × 10⁶ K¹
+30°C a +100°C (transversal) ISO 11359 110 × 10⁶ K¹
VICAT - Softening point
50N (heating rate 120°C/h) ISO 306 150 °C
HDT - Heat Deflection Temperature
0.45 MPa ISO 75 150 °C
1.81 MPa ISO 75 100 °C
Thermal conductivity
in plane ASTM E 1461-92 0.3 W/mK
through plane ASTM E 1461-92 0.3 W/mK
Flammability Standard Value Measure Units
Flammability rating
3 mm thickness UL 94 HB
1.5 mm thickness UL 94 HB
Electrical properties Standard Value Measure Units
CTI - Comparative Tracking Index - solution A (without surfactant) IEC 60112 600 V
Electrical resistivity
Surface, dry ASTM D 257 1E12 ohm
Dielectric strength (short period)
2 mm thickness, 23°C, dry ASTM D 149 16 kV/mm
Melt Temperature Standard Value Measure Units
Suggested melt temperature --- 190 ÷ 210 °C
Mould Temperature Standard Value Measure Units
Suggested mould temperature --- 80 ÷ 120 °C
Drying conditions (hot air dessiccator)
Predrying needed. At least 3 hours at 80 ÷ 120°C
Injection speed
Injection speed: medium to high. Setting an injection profile should improve moulding.
Hot runners
Usage of hot runner: possible