Family: LATAN
Base resin:Polyoximethylene (POM)
General information
Compound based on Polyoximethylene (POM). Toughened. PFAS-free product.
The products mentioned herein are not suitable for applications in contact with foodstuffs or for potable water transportation, or for toy manufacturing.
The products mentioned herein are not suitable for applications in the pharmaceutical, medical or dental sector.
Features
  • - Toughened
Process types
  • - Injection moulding
Download documents
Technical datasheets
  • IT
  • UK
  • US
  • DE
  • FR
  • ES
  • PT
Technical characteristics
Physical properties Standard Value Measure Units
Density ISO 1183 1.36 g/cm³
Linear shrinkage at moulding
Longitudinal (2.0mm/60MPa) ISO 294-4 2,30 ÷ 2,70 %
Transversal (2.0mm/60MPa) ISO 294-4 2,35 ÷ 2,75 %
Dimensional stability --- 70
Moisture absorption
Saturation, in air ISO 62-4 0.18 %
Mechanical properties Standard Value Measure Units
CHARPY impact strength
Notched, at +23°C ISO 179-1eA 10 kJ/m²
Tensile strength
At yield (5 mm/min), 23°C ISO 527 40 MPa
At yield (5 mm/min), 60°C ISO 527 25 MPa
At yield (5 mm/min), 90°C ISO 527 15 MPa
Elastic modulus
Tensile (1 mm/min), 23°C ISO 527 1500 MPa
Tensile (1 mm/min), 60°C ISO 527 900 MPa
Tensile (1 mm/min), 90°C ISO 527 500 MPa
Thermal properties Standard Value Measure Units
Coefficient of linear thermal expansion (CLTE)
+30°C to +100°C (longitudinal) ISO 11359 120 × 10⁶ K¹
+30°C a +100°C (transversal) ISO 11359 120 × 10⁶ K¹
VICAT - Softening point
50N (heating rate 120°C/h) ISO 306 130 °C
HDT - Heat Deflection Temperature
0.45 MPa ISO 75 120 °C
1.81 MPa ISO 75 65 °C
Thermal conductivity
in plane ASTM E 1461-92 0.2 W/mK
through plane ASTM E 1461-92 0.2 W/mK
Flammability Standard Value Measure Units
Flammability rating
3 mm thickness UL 94 HB
1.5 mm thickness UL 94 HB
Electrical properties Standard Value Measure Units
CTI - Comparative Tracking Index - solution A (without surfactant) IEC 60112 600 V
Electrical resistivity
Surface, dry ASTM D 257 1E12 ohm
Dielectric strength (short period)
2 mm thickness, 23°C, dry ASTM D 149 18 kV/mm
Melt Temperature Standard Value Measure Units
Suggested melt temperature --- 190 ÷ 210 °C
Mould Temperature Standard Value Measure Units
Suggested mould temperature --- 50 ÷ 80 °C
Drying conditions (hot air dessiccator)
Predrying needed. At least 4 hours at 80 ÷ 90°C
Injection speed
Injection speed: medium to high. Setting an injection profile should improve moulding.
Hot runners
Usage of hot runner: possible