LATICONTHER 62 CP7/700-V0HF1

Family: LATICONTHER
Base resin:Polyamide 6 (PA 6)
General information
High thermal conductivity product based on Polyamide 6 (PA 6). Special filler. Flame retardant, UL94 V-0 class, free of halogens-based flame retardants and red phosphorous. PFAS-free product.
The products mentioned herein are not suitable for applications in contact with foodstuffs or for potable water transportation, or for toy manufacturing.
The products mentioned herein are not suitable for applications in the pharmaceutical, medical or dental sector.
Features
  • - Thermally conductive
  • - Flame retardant, free of halogens-based flame retardants and red phosphorous
Project challenges
  • - Thermal conductivity
  • - Metal replacement
  • - Flame retardancy halogen free
Additives
  • - Ceramic fillers
Process types
  • - Injection moulding
Download documents
Technical datasheets
  • IT
  • UK
  • US
  • DE
  • FR
  • ES
  • PT
Technical characteristics
Physical properties Standard Value Measure Units
Density ISO 1183 1.77 g/cm³
Linear shrinkage at moulding
Longitudinal (2.0mm/60MPa) ISO 294-4 0.20 ÷ 0.50 %
Transversal (2.0mm/60MPa) ISO 294-4 0.40 ÷ 0.70 %
Dimensional stability --- 72
Moisture absorption
Saturation, in air ISO 62-4 0.7 %
Mechanical properties Standard Value Measure Units
CHARPY impact strength
Unnotched, at +23°C ISO 179-1eU 6 kJ/m²
Notched, at +23°C ISO 179-1eA 3 kJ/m²
Tensile elongation
At break (5 mm/min), 23°C ISO 527 0.6 %
Tensile strength
At break (5 mm/min), 23°C ISO 527 75 MPa
Elastic modulus
Tensile (1 mm/min), 23°C ISO 527 17000 MPa
Thermal properties Standard Value Measure Units
Coefficient of linear thermal expansion (CLTE)
+30°C to +100°C (longitudinal) ISO 11359 30 × 10⁶ K¹
+30°C a +100°C (transversal) ISO 11359 35 × 10⁶ K¹
VICAT - Softening point
50N (heating rate 120°C/h) ISO 306 205 °C
HDT - Heat Deflection Temperature
0.45 MPa ISO 75 210 °C
1.81 MPa ISO 75 200 °C
Thermal conductivity
in plane ASTM E 1461-92 4.3 W/mK
through plane ASTM E 1461-92 1.4 W/mK
Flammability Standard Value Measure Units
Flammability rating
3 mm thickness UL 94 V-0
1.5 mm thickness UL 94 V-0
0.75 mm thickness UL 94 V-2
GWFI - Glow Wire Flammability Index
2 mm thickness IEC 60695-2-12 960 °C
1 mm thickness IEC 60695-2-12 960 °C
GWIT - Glow Wire Ignition Test
2 mm thickness IEC 60695-2-13 775 °C
1 mm thickness IEC 60695-2-13 775 °C
Electrical properties Standard Value Measure Units
CTI - Comparative Tracking Index - solution A (without surfactant) IEC 60112 600 V
Electrical resistivity
Surface, dry ASTM D 257 1E12 ohm
Melt Temperature Standard Value Measure Units
Suggested melt temperature --- 250 ÷ 280 °C
Mould Temperature Standard Value Measure Units
Suggested mould temperature --- 80 ÷ 100 °C
Storage
PAY ATTENTION! Material is prone to absorb moisture.
Drying conditions (hot air dessiccator)
Predrying needed. At least 2 hours at 80 ÷ 100°C
Injection speed
Injection speed: medium to high. Setting an injection profile should improve moulding.
Hot runners
Usage of hot runner: to be evaluated