LATIECO 62 MR H2 G/20-V2HF GY:2778LU1-D

Family: LATIECO
Base resin:Polyamide 6 (PA 6)
General information
Product based on Polyamide 6 (PA 6) from mechanical recycling of PIR material. Improved thermal stabilisation. Glass fibres. Flame retardant, UL94 V-2 class, free of halogens-based flame retardants and red phosphorous. UV-Laserable version. PFAS-free product.
The products mentioned herein are not suitable for applications in contact with foodstuffs or for potable water transportation, or for toy manufacturing.
The products mentioned herein are not suitable for applications in the pharmaceutical, medical or dental sector.
Features
  • - Flame retardant, free of halogens-based flame retardants and red phosphorous
Sustainability
  • - Recycled based - mechanical
Project challenges
  • - Flame retardancy halogen free
Additives
  • - Glass fibres
Process types
  • - Injection moulding
Download documents
Technical datasheets
  • IT
  • UK
  • US
  • DE
  • FR
  • ES
  • PT
Technical characteristics
Physical properties Standard Value Measure Units
Density ISO 1183 1.34 g/cm³
Linear shrinkage at moulding
Longitudinal (2.0mm/60MPa) ISO 294-4 0.70 ÷ 1.00 %
Transversal (2.0mm/60MPa) ISO 294-4 0.70 ÷ 1.00 %
Dimensional stability --- 78
Moisture absorption
Saturation, in air ISO 62-4 2.2 %
Mechanical properties Standard Value Measure Units
CHARPY impact strength
Unnotched, at +23°C ISO 179-1eU 35 kJ/m²
Notched, at +23°C ISO 179-1eA 3.5 kJ/m²
Tensile elongation
At break (5 mm/min), 23°C ISO 527 3.4 %
Tensile strength
At break (5 mm/min), 23°C ISO 527 70 MPa
Elastic modulus
Tensile (1 mm/min), 23°C ISO 527 4500 MPa
Thermal properties Standard Value Measure Units
Coefficient of linear thermal expansion (CLTE)
+30°C to +100°C (longitudinal) ISO 11359 60 × 10⁶ K¹
+30°C a +100°C (transversal) ISO 11359 70 × 10⁶ K¹
VICAT - Softening point
50N (heating rate 120°C/h) ISO 306 205 °C
HDT - Heat Deflection Temperature
0.45 MPa ISO 75 200 °C
1.81 MPa ISO 75 150 °C
Flammability Standard Value Measure Units
Flammability rating
3 mm thickness UL 94 V-2
1.5 mm thickness UL 94 V-2
0.75 mm thickness UL 94 V-2
GWFI - Glow Wire Flammability Index
2 mm thickness IEC 60695-2-12 960 °C
1 mm thickness IEC 60695-2-12 960 °C
GWIT - Glow Wire Ignition Test
2 mm thickness IEC 60695-2-13 725 °C
1 mm thickness IEC 60695-2-13 725 °C
Electrical properties Standard Value Measure Units
CTI - Comparative Tracking Index - solution A (without surfactant) IEC 60112 425 V
Electrical resistivity
Surface, dry ASTM D 257 1E12 ohm
Dielectric strength (short period)
2 mm thickness, 23°C, dry ASTM D 149 21 kV/mm
Melt Temperature Standard Value Measure Units
Suggested melt temperature --- 240 ÷ 250 °C
Mould Temperature Standard Value Measure Units
Suggested mould temperature --- 60 ÷ 90 °C
Storage
PAY ATTENTION! Material is prone to absorb moisture.
Drying conditions (hot air dessiccator)
Predrying needed. At least 2 hours at 70 ÷ 90°C
Injection speed
Injection speed: medium. Setting an injection profile should improve moulding.
Hot runners
Usage of hot runner: to be evaluated