LATIGRAY B01-01 AM CX/35 F1

Family: LATI AM
Base resin:Bio-polymer resin
General information
Radiopaque compound based on Bio-polymer resin. 3D printing version. Special filler. PFAS-free product.
Versions of product mentioned herein are suitable for applications in contact with foodstuffs or for toy manufacturing. Nevertheless, manufactured parts have to be verified according to the specific directives.
The products mentioned herein are not suitable for applications in the pharmaceutical, medical or dental sector.
Features
  • - Radiopaque / X-ray shielding
Project challenges
  • - X-Ray detectability
Additives
  • - Ceramic fillers
Process types
  • - 3D Printing
Download documents
Technical datasheets
  • IT
  • UK
  • US
  • DE
  • FR
  • ES
  • PT
Technical characteristics
Physical properties Standard Value Measure Units
Density ISO 1183 1.66 g/cm³
Linear shrinkage at moulding
Longitudinal (2.0mm/60MPa) ISO 294-4 0,15 ÷ 0,40 %
Transversal (2.0mm/60MPa) ISO 294-4 0,15 ÷ 0,40 %
Dimensional stability --- 66
Moisture absorption
Saturation, in air ISO 62-4 0.6 %
Mechanical properties Standard Value Measure Units
CHARPY impact strength
Unnotched, at +23°C ISO 179-1eU 12 kJ/m²
Notched, at +23°C ISO 179-1eA 2 kJ/m²
Tensile elongation
At break (5 mm/min), 23°C ISO 527 3.5 %
Tensile strength
At break (5 mm/min), 23°C ISO 527 35 MPa
Elastic modulus
Tensile (1 mm/min), 23°C ISO 527 7000 MPa
Thermal properties Standard Value Measure Units
Coefficient of linear thermal expansion (CLTE)
+30°C to +100°C (longitudinal) ISO 11359 70 × 10⁶ K¹
+30°C a +100°C (transversal) ISO 11359 70 × 10⁶ K¹
VICAT - Softening point
50N (heating rate 120°C/h) ISO 306 60 °C
HDT - Heat Deflection Temperature
0.45 MPa ISO 75 55 °C
1.81 MPa ISO 75 50 °C
Electrical properties Standard Value Measure Units
Electrical resistivity
Surface, dry ASTM D 257 1E12 ohm
Melt Temperature Standard Value Measure Units
Suggested melt temperature --- NULL °C
Mould Temperature Standard Value Measure Units
Suggested mould temperature --- NULL °C
Drying conditions (hot air dessiccator)
Predrying needed. At least 4 hours at 60°C
Injection speed
Injection speed: NULL. Setting an injection profile should improve moulding.
Hot runners
Usage of hot runner: not suggested