Family: LATILON
Base resin:Polycarbonate (PC)
General information
Compound based on Polycarbonate (PC). Glass fibres.
The products mentioned herein are not suitable for applications in contact with foodstuffs or for potable water transportation, or for toy manufacturing.
Versions of product mentioned herein may support applications in the pharmaceutical, medical or dental sector. Nevertheless, manufactured parts have to be verified according to the specific directives.
Project challenges
- - Improved resilience at low temperature
- - Wear and friction
Additives
- - Glass fibres
Process types
- - Injection moulding
Download documents
Technical datasheets
- IT
- UK
- US
- DE
- FR
- ES
- PT
Technical characteristics
| Physical properties | Standard | Value | Measure Units |
|---|---|---|---|
| Density | ISO 1183 | 1.33 | g/cm³ |
| Linear shrinkage at moulding | |||
| Longitudinal (2.0mm/60MPa) | ISO 294-4 | 0.20 ÷ 0.40 | % |
| Transversal (2.0mm/60MPa) | ISO 294-4 | 0.50 ÷ 0.80 | % |
| Dimensional stability | --- | 52 | |
| Moisture absorption | |||
| Saturation, in air | ISO 62-4 | 0.13 | % |
| Mechanical properties | Standard | Value | Measure Units |
| CHARPY impact strength | |||
| Unnotched, at +23°C | ISO 179-1eU | 40 | kJ/m² |
| Notched, at +23°C | ISO 179-1eA | 9 | kJ/m² |
| Tensile elongation | |||
| At break (5 mm/min), 23°C | ISO 527 | 3.2 | % |
| At break (5 mm/min), 60°C | ISO 527 | 3 | % |
| At break (5 mm/min), 90°C | ISO 527 | 2.8 | % |
| At break (5 mm/min), 120°C | ISO 527 | 2.6 | % |
| Tensile strength | |||
| At break (5 mm/min), 23°C | ISO 527 | 100 | MPa |
| At break (5 mm/min), 60°C | ISO 527 | 85 | MPa |
| At break (5 mm/min), 90°C | ISO 527 | 70 | MPa |
| At break (5 mm/min), 120°C | ISO 527 | 55 | MPa |
| Elastic modulus | |||
| Tensile (1 mm/min), 23°C | ISO 527 | 5800 | MPa |
| Tensile (1 mm/min), 60°C | ISO 527 | 5300 | MPa |
| Tensile (1 mm/min), 90°C | ISO 527 | 5000 | MPa |
| Tensile (1 mm/min), 120°C | ISO 527 | 4800 | MPa |
| Thermal properties | Standard | Value | Measure Units |
| Coefficient of linear thermal expansion (CLTE) | |||
| +30°C to +100°C (longitudinal) | ISO 11359 | 25 | × 10ˉ⁶ Kˉ¹ |
| +30°C a +100°C (transversal) | ISO 11359 | 55 | × 10ˉ⁶ Kˉ¹ |
| VICAT - Softening point | |||
| 50N (heating rate 120°C/h) | ISO 306 | 145 | °C |
| HDT - Heat Deflection Temperature | |||
| 0.45 MPa | ISO 75 | 140 | °C |
| 1.81 MPa | ISO 75 | 135 | °C |
| Flammability | Standard | Value | Measure Units |
| Oxygen Index | ASTM D 2863 | 33 | % |
| Flammability rating | |||
| 1.5 mm thickness | UL 94 | V-1 | |
| Electrical properties | Standard | Value | Measure Units |
| Electrical resistivity | |||
| Surface, dry | ASTM D 257 / D 4496 | 1E12 | ohm |
| Dielectric strength (short period) | |||
| 2 mm thickness, 23°C, dry | ASTM D 149 | 20 | kV/mm |
| Melt Temperature | Standard | Value | Measure Units |
| Suggested melt temperature | --- | 290 ÷ 300 | °C |
| Mould Temperature | Standard | Value | Measure Units |
| Suggested mould temperature | --- | 100 ÷ 120 | °C |
Drying conditions (hot air dessiccator)
Predrying needed. At least 3 hours at 110 ÷ 120°C
Injection speed
Injection speed: medium to high. Setting an injection profile should improve moulding.
Hot runners
Usage of hot runner: possible