Family: LATI AM
Base resin:Bio-polymer resin
General information
Semiconductive/dissipative product based on Bio-polymer resin. 3D printing version. Carbon nanotubes. PFAS-free product.
The products mentioned herein are not suitable for applications in contact with foodstuffs or for potable water transportation, or for toy manufacturing.
The products mentioned herein are not suitable for applications in the pharmaceutical, medical or dental sector.
Features
- - Flame retardant, with red phosphorous
- - EMI shielding
Project challenges
- - Electrical dissipation
- - High temperature usage
- - EMI shielding
Additives
- - Carbon Nanotubes
Process types
- - Injection moulding
Download documents
Technical datasheets
- IT
- UK
- US
- DE
- FR
- ES
- PT
Technical characteristics
| Physical properties | Standard | Value | Measure Units |
|---|---|---|---|
| Density | ISO 1183 | 1.34 | g/cm³ |
| Mechanical properties | Standard | Value | Measure Units |
| CHARPY impact strength | |||
| Unnotched, at +23°C | ISO 179-1eU | 45 | kJ/m² |
| Notched, at +23°C | ISO 179-1eA | 5 | kJ/m² |
| Tensile elongation | |||
| At break (5 mm/min), 23°C | ISO 527 | 2.5 | % |
| Tensile strength | |||
| At break (5 mm/min), 23°C | ISO 527 | 20 | MPa |
| Elastic modulus | |||
| Tensile (1 mm/min), 23°C | ISO 527 | 800 | MPa |
| Thermal properties | Standard | Value | Measure Units |
| Coefficient of linear thermal expansion (CLTE) | |||
| +30°C to +100°C (longitudinal) | ISO 11359 | 75 | × 10ˉ⁶ Kˉ¹ |
| VICAT - Softening point | |||
| 50N (heating rate 120°C/h) | ISO 306 | 55 | °C |
| HDT - Heat Deflection Temperature | |||
| 0.45 MPa | ISO 75 | 50 | °C |
| 1.81 MPa | ISO 75 | 40 | °C |
| Electrical properties | Standard | Value | Measure Units |
| Electrical resistivity | |||
| Surface, dry | ASTM D 257 / D 4496 | 5E0 | ohm |
| Melt Temperature | Standard | Value | Measure Units |
| Suggested melt temperature | --- | NULL | °C |
| Mould Temperature | Standard | Value | Measure Units |
| Suggested mould temperature | --- | NULL | °C |
Drying conditions (hot air dessiccator)
Predrying needed. At least 4 hours at 60°C
Injection speed
Injection speed: NULL. Setting an injection profile should improve moulding.
Hot runners
Usage of hot runner: not suggested
LATIOHM B61-01 AM CNT