Family: LATISTAT
Base resin:Polypropylene copolymer (PPc)
General information
Dissipative product based on Polypropylene copolymer (PPc). PFAS-free product.
The products mentioned herein are not suitable for applications in contact with foodstuffs or for potable water transportation, or for toy manufacturing.
The products mentioned herein are not suitable for applications in the pharmaceutical, medical or dental sector.
Features
  • - Anti-static or dissipative
Project challenges
  • - Electrical dissipation
Process types
  • - Injection moulding
Download documents
Technical datasheets
  • IT
  • UK
  • US
  • DE
  • FR
  • ES
  • PT
Technical characteristics
Physical properties Standard Value Measure Units
Density ISO 1183 1 g/cm³
Linear shrinkage at moulding
Longitudinal (2.0mm/60MPa) ISO 294-4 1.20 ÷ 1.40 %
Transversal (2.0mm/60MPa) ISO 294-4 1.40 ÷ 1.70 %
Dimensional stability --- 75
Moisture absorption
Saturation, in air ISO 62-4 0.08 %
Mechanical properties Standard Value Measure Units
CHARPY impact strength
Notched, at +23°C ISO 179-1eA 15 kJ/m²
Notched, at -20°C ISO 179-1eA 3.5 kJ/m²
Tensile elongation
At yield (5 mm/min), 60°C ISO 527 7.8 %
At yield (5 mm/min), 90°C ISO 527 10 %
At break (5 mm/min), 23°C ISO 527 4.1 %
At break (5 mm/min), 60°C ISO 527 9 %
Tensile strength
At yield (5 mm/min), 60°C ISO 527 15 MPa
At yield (5 mm/min), 90°C ISO 527 10 MPa
At break (5 mm/min), 23°C ISO 527 23 MPa
At break (5 mm/min), 60°C ISO 527 15 MPa
At break (5 mm/min), 90°C ISO 527 5 MPa
Elastic modulus
Tensile (1 mm/min), 23°C ISO 527 1600 MPa
Tensile (1 mm/min), 60°C ISO 527 780 MPa
Tensile (1 mm/min), 90°C ISO 527 360 MPa
Thermal properties Standard Value Measure Units
Coefficient of linear thermal expansion (CLTE)
+30°C to +100°C (longitudinal) ISO 11359 110 × 10ˉ⁶ Kˉ¹
+30°C a +100°C (transversal) ISO 11359 110 × 10ˉ⁶ Kˉ¹
VICAT - Softening point
50N (heating rate 120°C/h) ISO 306 90 °C
HDT - Heat Deflection Temperature
0.45 MPa ISO 75 90 °C
1.81 MPa ISO 75 55 °C
Electrical properties Standard Value Measure Units
Electrical resistivity
Surface, dry ASTM D 257 / D 4496 2E1 ohm
Melt Temperature Standard Value Measure Units
Suggested melt temperature --- 190 ÷ 220 °C
Mould Temperature Standard Value Measure Units
Suggested mould temperature --- 20 ÷ 50 °C
Drying conditions (hot air dessiccator)
Predrying needed. At least 2 hours at 80 ÷ 90°C
Injection speed
Injection speed: medium. Setting an injection profile should improve moulding.
Hot runners
Usage of hot runner: possible