Physical Properties	Standard	SI Units
Density	ISO 1183	1.28 g/cm3
Linear shrinkage at moulding - 2.0 mm th. (at 60 MPa of cavity pressure) *
Longitudinal	ISO 294-4	0.6 - 1 %
Transversal	ISO 294-4	0.6 - 1 %
* Values obtained according to ISO norm at the specified pressure. Actual shrinkage values may differ because of the design.

Mechanical Properties	Standard	SI Units
CHARPY impact strength (sample 80x10x4 mm)
Unnotched, at 23°C	ISO 179-1eU	100 kJ/m2
Notched, at 23°C	ISO 179-1eA	5 kJ/m2
Tensile elongation (speed 5 mm/min)
At yield	ISO 527 (1)	12 %
At break, 23°C	ISO 527 (1)	18 %
Tensile strength (speed 5 mm/min)
At yield	ISO 527 (1)	60 MPa
At break, 23°C	ISO 527 (1)	60 MPa
Elastic modulus
Tensile (speed 1 mm/min), 23°C	ISO 527 (1)	2850 MPa

Thermal Properties	Standard	SI Units
Coefficient of linear thermal expansion (CLTE)
+30°C to +100°C (longitudinal)	ISO 11359-2	135 μm/(m·ºC)
VICAT - Softening point - 50 N (heating rate 50°C/h)	ISO 306	250°C
HDT - Heat Deflection Temperature
0,45 MN/m2	ISO 75	250 °C
1,81 MN/m2	ISO 75	230 °C

Moulding Parameters	Standard	SI Units
Predrying (LATIGEA: at least 6 hours, other families: at least 3 hours)		90 - 100 °C
Cylinder Temperature		270 - 290 °C
Mould Temperature		80 - 100 °C
Injection Speed		Medium
Hot Runner Moulds		Allowed

The products mentioned herein are not suitable for applications in the pharmaceutical, medical or dental sector.   Versions of product mentioned herein are suitable for applications in contact with foodstuff or for potable water transportation, or for toy manufacturing. However, manufactured parts have to be verified according to the specific directives.