Physical Properties	Standard	SI Units
Density	ISO 1183	1.01 g/cm3
Linear shrinkage at moulding - 2.0 mm th. (at 60 MPa of cavity pressure) *
Longitudinal	ISO 294-4	1.2 - 1.5 %
Transversal	ISO 294-4	1.2 - 1.5 %
Dimensional Stability **		70
Moisture absorption (after 24h)	ISO62	0.07 %
* Values obtained according to ISO norm at the specified pressure. Actual shrinkage values may differ because of the design.
** Planarity index based on differential shrinkage and edge warpage. Index: 00÷30 30÷50 50÷70 70÷90 90÷100 Rating: POOR MODERATE FAIR GOOD VERY GOOD

Mechanical Properties	Standard	SI Units
CHARPY impact strength (sample 80x10x4 mm)
Unnotched, at 23°C	ISO 179-1eU	25 kJ/m2
Notched, at 23°C	ISO 179-1eA	2 kJ/m2
Tensile elongation (speed 5 mm/min)
At yield	ISO 527 (1)	5 %
At break, 23°C	ISO 527 (1)	20 %
At break, 60°C	ISO 527 (1)	>100,0 %
At break, 90°C	ISO 527 (1)	>100,0 %
Tensile strength (speed 5 mm/min)
At yield	ISO 527 (1)	20 MPa
At break, 23°C	ISO 527 (1)	15 MPa
At break, 60°C	ISO 527 (1)	NR MPa
At break, 90°C	ISO 527 (1)	NR MPa
Elastic modulus
Tensile (speed 1 mm/min), 23°C	ISO 527 (1)	1800 MPa
Tensile (speed 1 mm/min), 60°C	ISO 527 (1)	800 MPa
Tensile (speed 1 mm/min), 90°C	ISO 527 (1)	500 MPa

Thermal Properties	Standard	SI Units
Coefficient of linear thermal expansion (CLTE)
+30°C to +100°C (longitudinal)	ISO 11359-2	120 μm/(m·ºC)
VICAT - Softening point - 50 N (heating rate 50°C/h)	ISO 306	100°C
HDT - Heat Deflection Temperature
0,45 MN/m2	ISO 75	110 °C
1,81 MN/m2	ISO 75	65 °C
C.U.T. - Continuous Use Temperature (20.000h)		100 °C

Flammability	Standard	SI Units
Oxygen Index	ASTM D 2863	33 %
Flammability Rating
3.00 mm thickness	UL 94	Class V-0
1.50 mm thickness	UL 94	Class V-0
0.75 mm thickness	UL 94	Class V-2
GWFI - Glow Wire Flammability Index
1.00 mm thickness	IEC 695-2-12	GWFI: 960/1.0
2.00 mm thickness	IEC 695-2-12	GWFI: 960/2.0
GWIT - Glow Wire Ignition Test
1.00 mm thickness	IEC 695-2-13	GWIT: 825/1.0
2.00 mm thickness	IEC 695-2-13	GWIT: 825/2.0

Electrical Properties	Standard	SI Units
CTI - Comparative Tracking Index (solution A - without surfactant)	IEC 112	600 V
Surface Resistivity	ASTM D 257	>1E10 ohm

LIST OF CERTIFICATIONS

UL approvals - long and short term performance (flammability, glow wire, RTI etc.)

* Please ensure that listed certificates are valid for the chosen product.

Moulding Parameters	Standard	SI Units
Predrying (LATIGEA: at least 6 hours, other families: at least 3 hours)		80 - 90 °C
Cylinder Temperature		180 - 210 °C
Mould Temperature		20 - 40 °C
Injection Speed		Medium
Hot Runner Moulds		Possible

The products mentioned herein are not suitable for applications in the pharmaceutical, medical or dental sector.   The products mentioned herein are not suitable for applications in contact with foodstuff or for potable water transportation, or for toy manufacturing.   The material must not be used to produce parts operating in hot (> 70°C / 160°F), very humid environments, or in contact with hot water, or in contact with overheated steam.   For applications in one of these fields, please contact our Technical Service.