Physical Properties	Standard	SI Units
Density	ISO 1183	1.52 g/cm3
Linear shrinkage at moulding - 2.0 mm th. (at 60 MPa of cavity pressure) *
Longitudinal	ISO 294-4	0.3 - 0.55 %
Transversal	ISO 294-4	1 - 1.3 %
Dimensional Stability **		45
Moisture absorption (after 24h)	ISO62	0.05 %
* Values obtained according to ISO norm at the specified pressure. Actual shrinkage values may differ because of the design.
** Planarity index based on differential shrinkage and edge warpage. Index: 00÷30 30÷50 50÷70 70÷90 90÷100 Rating: POOR MODERATE FAIR GOOD VERY GOOD

Mechanical Properties	Standard	SI Units
CHARPY impact strength (sample 80x10x4 mm)
Unnotched, at 23°C	ISO 179-1eU	55 kJ/m2
Notched, at 23°C	ISO 179-1eA	8 kJ/m2
Tensile elongation (speed 5 mm/min)
At break, 23°C	ISO 527 (1)	2.5 %
At break, 60°C	ISO 527 (1)	3 %
At break, 90°C	ISO 527 (1)	3.6 %
At break, 120°C	ISO 527 (1)	4.2 %
At break, 150°C	ISO 527 (1)	5 %
Tensile strength (speed 5 mm/min)
At break, 23°C	ISO 527 (1)	135 MPa
At break, 60°C	ISO 527 (1)	95 MPa
At break, 90°C	ISO 527 (1)	85 MPa
At break, 120°C	ISO 527 (1)	65 MPa
At break, 150°C	ISO 527 (1)	55 MPa
Elastic modulus
Tensile (speed 1 mm/min), 23°C	ISO 527 (1)	9500 MPa
Tensile (speed 1 mm/min), 60°C	ISO 527 (1)	7900 MPa
Tensile (speed 1 mm/min), 90°C	ISO 527 (1)	6800 MPa
Tensile (speed 1 mm/min), 120°C	ISO 527 (1)	5000 MPa
Tensile (speed 1 mm/min), 150°C	ISO 527 (1)	3900 MPa

Thermal Properties	Standard	SI Units
Coefficient of linear thermal expansion (CLTE)
+30°C to +100°C (longitudinal)	ISO 11359-2	40 μm/(m·ºC)
VICAT - Softening point - 50 N (heating rate 50°C/h)	ISO 306	215°C
HDT - Heat Deflection Temperature
0,45 MN/m2	ISO 75	220 °C
1,81 MN/m2	ISO 75	210 °C
C.U.T. - Continuous Use Temperature (20.000h)		135 °C

Electrical Properties	Standard	SI Units
Surface Resistivity	ASTM D 257	>1E10 ohm

LIST OF CERTIFICATIONS

UL approvals - long and short term performance (flammability, glow wire, RTI etc.)

* Please ensure that listed certificates are valid for the chosen product.

Moulding Parameters	Standard	SI Units
Predrying (LATIGEA: at least 6 hours, other families: at least 3 hours)		110 - 130 °C
Cylinder Temperature		240 - 250 °C
Mould Temperature		70 - 90 °C
Injection Speed		Medium
Hot Runner Moulds		Allowed

The products mentioned herein are not suitable for applications in the pharmaceutical, medical or dental sector.   The products mentioned herein are not suitable for applications in contact with foodstuff or for potable water transportation, or for toy manufacturing.   For applications in one of these fields, please contact our Technical Service.