LATIGLOSS 57 G/50 F2
|
Product with high mechanical properties and exceptional surface finish based on Semi...
Change Units: |
SI
US
Physical
Mechanical
Thermal
Electrical
Certifications
Moulding
Download
Physical Properties
Standard
SI Units
Density
ISO 1183
1.63
g/cm
3
Linear shrinkage at moulding - 2.0 mm th. (at 60 MPa of cavity pressure) *
Longitudinal
ISO 294-4
0.15 - 0.3
%
Transversal
ISO 294-4
0.3 - 0.5
%
* Values obtained according to ISO norm at the specified pressure. Actual shrinkage values may differ because of the design.
Mechanical Properties
Standard
SI Units
CHARPY impact strength (sample 80x10x4 mm)
Unnotched, at 23°C
ISO 179-1eU
70
kJ/m
2
Notched, at 23°C
ISO 179-1eA
9
kJ/m
2
Tensile elongation (speed 5 mm/min)
At break, 23°C
ISO 527 (1)
1.8
%
At break, 60°C
ISO 527 (1)
2
%
At break, 90°C
ISO 527 (1)
2.1
%
At break, 120°C
ISO 527 (1)
3.5
%
At break, 150°C
ISO 527 (1)
6
%
Tensile strength (speed 5 mm/min)
At break, 23°C
ISO 527 (1)
240
MPa
At break, 60°C
ISO 527 (1)
225
MPa
At break, 90°C
ISO 527 (1)
190
MPa
At break, 120°C
ISO 527 (1)
130
MPa
At break, 150°C
ISO 527 (1)
70
MPa
Elastic modulus
Tensile (speed 1 mm/min), 23°C
ISO 527 (1)
18000
MPa
Tensile (speed 1 mm/min), 60°C
ISO 527 (1)
15500
MPa
Tensile (speed 1 mm/min), 90°C
ISO 527 (1)
14000
MPa
Tensile (speed 1 mm/min), 120°C
ISO 527 (1)
11000
MPa
Tensile (speed 1 mm/min), 150°C
ISO 527 (1)
5500
MPa
Thermal Properties
Standard
SI Units
Coefficient of linear thermal expansion (CLTE)
+30°C to +100°C (longitudinal)
ISO 11359-2
10
μm/(m·ºC)
VICAT - Softening point - 50 N (heating rate 50°C/h)
ISO 306
260
°C
HDT - Heat Deflection Temperature
0,45 MN/m
2
ISO 75
285
°C
1,81 MN/m
2
ISO 75
260
°C
C.U.T. - Continuous Use Temperature (20.000h)
150
°C
Electrical Properties
Standard
SI Units
Surface Resistivity
ASTM D 257
>1E10
ohm
LIST OF CERTIFICATIONS
ACS approvals (Attestation de Conformité Sanitaire standard XP P 41-250) - Migration tests on material for drinkable water contact applications
DVGW W270 approvals - Microbial growth on material to come in contact with drinkable water
KTW approvals - Migration tests on material to come in contact with drinkable water
NFS/ANSI 61 approvals - US standard for drinkable water contact applications
WRAS approvals (Water Regulation Advisory Scheme BS 6920) - Material for drinkable water applications
* Please ensure that listed certificates are valid for the chosen product.
Moulding Parameters
Standard
SI Units
Predrying (LATIGEA: at least 6 hours, other families: at least 3 hours)
120 - 130
°C
Cylinder Temperature
310 - 340
°C
Mould Temperature
150 - 170
°C
Injection Speed
Medium
Hot Runner Moulds
Allowed
The products mentioned herein are not suitable for applications in the pharmaceutical, medical or dental sector.
Versions of product mentioned herein are suitable for applications in contact with foodstuff or for potable water transportation, or for toy manufacturing. However, manufactured parts have to be verified according to the specific directives.
DOWNLOAD
LATIGLOSS 57 G/50 F2 - Italian, SI Units
LATIGLOSS 57 G/50 F2 - English, SI Units
LATIGLOSS 57 G/50 F2 - English, Imperial (US) Units
LATIGLOSS 57 G/50 F2 - German, SI Units
LATIGLOSS 57 G/50 F2 - French, SI Units
LATIGLOSS 57 G/50 F2 - Spanish, SI Units
LATIGLOSS 57 G/50 F2 - Portuguese, SI Units
LET01b - Relased 10/03/2016
Privacy & cookie
l
Terms & Conditions
Copyright © 2018 - LATI Industria Termoplastici S.p.A. - Registered office: via F. Baracca, 7 - I - 21040 VEDANO OLONA (VA) ITALY
Share Capital € 3.818.400 i.v. - C.F., P. IVA e Reg. Impr. di VA n. 00214880122 - Codice Destinatario SDI: K1L103O
R.E.A. di Varese n. 41557 - E-mail:
info@lati.com
- PEC:
lati@pec.net
- Tel. +39-0332 409111 - Fax +39-0332 409235/307