Physical Properties	Standard	SI Units
Density	ISO 1183	1.67 g/cm3
Linear shrinkage at moulding - 2.0 mm th. (at 60 MPa of cavity pressure) *
Longitudinal	ISO 294-4	0.2 - 0.35 %
Transversal	ISO 294-4	0.45 - 0.65 %
Moisture absorption (after 24h)	ISO62	0.04 %
* Values obtained according to ISO norm at the specified pressure. Actual shrinkage values may differ because of the design.

Mechanical Properties	Standard	SI Units
CHARPY impact strength (sample 80x10x4 mm)
Unnotched, at 23°C	ISO 179-1eU	30 kJ/m2
Notched, at 23°C	ISO 179-1eA	9 kJ/m2
Tensile elongation (speed 5 mm/min)
At break, 23°C	ISO 527 (1)	1.4 %
At break, 60°C	ISO 527 (1)	1.5 %
At break, 90°C	ISO 527 (1)	2 %
At break, 120°C	ISO 527 (1)	3 %
At break, 150°C	ISO 527 (1)	3.4 %
Tensile strength (speed 5 mm/min)
At break, 23°C	ISO 527 (1)	180 MPa
At break, 60°C	ISO 527 (1)	170 MPa
At break, 90°C	ISO 527 (1)	140 MPa
At break, 120°C	ISO 527 (1)	100 MPa
At break, 150°C	ISO 527 (1)	75 MPa
Elastic modulus
Tensile (speed 1 mm/min), 23°C	ISO 527 (1)	16000 MPa
Tensile (speed 1 mm/min), 60°C	ISO 527 (1)	15500 MPa
Tensile (speed 1 mm/min), 90°C	ISO 527 (1)	15000 MPa
Tensile (speed 1 mm/min), 120°C	ISO 527 (1)	9800 MPa
Tensile (speed 1 mm/min), 150°C	ISO 527 (1)	6800 MPa

Thermal Properties	Standard	SI Units
Coefficient of linear thermal expansion (CLTE)
+30°C to +100°C (longitudinal)	ISO 11359-2	10 μm/(m·ºC)
VICAT - Softening point - 50 N (heating rate 50°C/h)	ISO 306	255°C
HDT - Heat Deflection Temperature
0,45 MN/m2	ISO 75	280 °C
1,81 MN/m2	ISO 75	270 °C
C.U.T. - Continuous Use Temperature (20.000h)		220 °C

Flammability	Standard	SI Units
Oxygen Index	ASTM D 2863	44 %
Flammability Rating
3.00 mm thickness	UL 94	Class V-0
1.50 mm thickness	UL 94	Class V-0
0.75 mm thickness	UL 94	Class V-0
GWFI - Glow Wire Flammability Index
1.00 mm thickness	IEC 695-2-12	GWFI: 960/1.0
2.00 mm thickness	IEC 695-2-12	GWFI: 960/2.0
GWIT - Glow Wire Ignition Test
1.00 mm thickness	IEC 695-2-13	GWIT: 775/1.0
2.00 mm thickness	IEC 695-2-13	GWIT: 775/2.0

Electrical Properties	Standard	SI Units
CTI - Comparative Tracking Index (solution A - without surfactant)	IEC 112	125 V
Surface Resistivity	ASTM D 257	>1E10 ohm

LIST OF CERTIFICATIONS

NFS/ANSI 51 approvals - US standard for food contact applications  UL approvals - long and short term performance (flammability, glow wire, RTI etc.)  WRAS approvals (Water Regulation Advisory Scheme BS 6920) - Material for drinkable water applications

* Please ensure that listed certificates are valid for the chosen product.

Moulding Parameters	Standard	SI Units
Predrying (LATIGEA: at least 6 hours, other families: at least 3 hours)		100 - 130 °C
Cylinder Temperature		290 - 310 °C
Mould Temperature		130 - 140 °C
Injection Speed		Medium - High
Hot Runner Moulds		Allowed

Versions of product mentioned herein may support applications in the pharmaceutical, medical or dental sector. However, manufactured parts have to be verified according to the specific directives.   Versions of product mentioned herein are suitable for applications in contact with foodstuff or for potable water transportation, or for toy manufacturing. However, manufactured parts have to be verified according to the specific directives.